| Items |
 /Asset/-008-ALUMINUM.JPG 1010 0.0080 Inch (in) Thickness 1100 Alloy H14 Half Hard Temper Aluminum |
 /Asset/-010-ALUMINUM.JPG 1199 0.0100 Inch (in) Thickness 1100 Alloy H14 Half Hard Temper Aluminum |
 /Asset/-012-ALUMINUM.JPG 1200 0.0120 Inch (in) Thickness 1100 Alloy H14 Half Hard Temper Aluminum |
 /Asset/-016-ALUMINUM.JPG 1201 0.0160 Inch (in) Thickness 1100 Alloy H14 Half Hard Temper Aluminum |
 /Asset/-020-ALUMINUM.JPG 1202 0.0200 Inch (in) Thickness 1100 Alloy H14 Half Hard Temper Aluminum |
|||||
| Description | ||||||||||
| Brands | Thin Metal Sales | |||||||||
| Width | Custom | |||||||||
| Length | Custom | |||||||||
| Alloy | 1100 Aluminum Alloy | |||||||||
| Thickness | 0.0080 in | 0.0100 in | 0.0120 in | 0.0160 in | 0.0200 in | |||||
| Thickness Tolerance | 0.0008 in | |||||||||
| ASTM Steel Standard | ASTM-B-209 | |||||||||
| Temper | H14 Half Hard Temper | |||||||||
| Maximum Silicon + Iron Composition | 0.95 % | |||||||||
| Maximum Manganese Composition | 0.05 % | |||||||||
| Maximum Copper Composition | 0.20 % | |||||||||
| Minimum Tensile Strength | 16,000 psi | |||||||||
| Maximum Zinc Composition | 0.10 % | |||||||||
| Maximum Others Composition (Each) | 0.05 % | |||||||||
| Maximum Others Composition (Total) | 0.15 % | |||||||||
| Minimum Yield Strength | 14,000 psi | |||||||||
| Maximum Tensile Strength | 21,000 psi | |||||||||
| Minimum Elongation (0.009 to 0.012 Inch (in) Thick) | 1 % | |||||||||
| Minimum Elongation (0.013 to 0.019 Inch (in) Thick) | 2 % | |||||||||
| Minimum Elongation (0.020 to 0.031 Inch (in) Thick) | 3 % | |||||||||
|
|
||||||||||