 1043 0.0080 Inch (in) Thickness 5052 Alloy H34 Half Hard Temper Aluminum |
 1226 0.0100 Inch (in) Thickness 5052 Alloy H34 Half Hard Temper Aluminum |
 1227 0.0120 Inch (in) Thickness 5052 Alloy H34 Half Hard Temper Aluminum |
 1228 0.0160 Inch (in) Thickness 5052 Alloy H34 Half Hard Temper Aluminum |
 1229 0.0200 Inch (in) Thickness 5052 Alloy H34 Half Hard Temper Aluminum |
|||||
| Description | ||||||||||
| Brands | Thin Metal Sales | |||||||||
| Width | Custom | |||||||||
| Length | Custom | |||||||||
| Alloy | 5052 Aluminum Alloy | |||||||||
| Thickness | 0.0080 in | 0.0100 in | 0.0120 in | 0.0160 in | 0.0200 in | |||||
| Thickness Tolerance | 0.0008 in | |||||||||
| ASTM Steel Standard | ASTM-B-209 | |||||||||
| Temper | H34 Half Hard Temper | |||||||||
| Maximum Manganese Composition | 0.10 % | |||||||||
| Maximum Silicon Composition | 0.25 % | |||||||||
| Maximum Chromium Composition | 0.35 % | |||||||||
| Maximum Copper Composition | 0.10 % | |||||||||
| Minimum Tensile Strength | 34,000 psi | |||||||||
| Maximum Iron Composition | 0.40 % | |||||||||
| Maximum Magnesium Composition | 2.80 % | |||||||||
| Maximum Zinc Composition | 0.10 % | |||||||||
| Maximum Others Composition (Each) | 0.05 % | |||||||||
| Maximum Others Composition (Total) | 0.15 % | |||||||||
| Minimum Yield Strength | 26,000 psi | |||||||||
| Maximum Tensile Strength | 41,000 psi | |||||||||
| Minimum Elongation (0.009 to 0.019 Inch (in) Thick) | 3 % | |||||||||
| Minimum Elongation (0.020 to 0.050 Inch (in) Thick) | 4 % | |||||||||
|
|
||||||||||