 1180 0.0020 Inch (in) Thickness T321 Alloy Annealed Temper Stainless Steel |
 1348 0.0030 Inch (in) Thickness T321 Alloy Annealed Temper Stainless Steel |
 1349 0.0040 Inch (in) Thickness T321 Alloy Annealed Temper Stainless Steel |
 1350 0.0050 Inch (in) Thickness T321 Alloy Annealed Temper Stainless Steel |
 1351 0.0060 Inch (in) Thickness T321 Alloy Annealed Temper Stainless Steel |
|||||
| Description | ||||||||||
| Brands | Thin Metal Sales | |||||||||
| Width | Custom | |||||||||
| Length | Custom | |||||||||
| Alloy | T321 Stainless Steel Alloy | |||||||||
| Thickness | 0.0020 in | 0.0030 in | 0.0040 in | 0.0050 in | 0.0060 in | |||||
| Thickness Tolerance | 10 % | 10 % | 5 % | 5 % | 5 % | |||||
| ASTM Steel Standard | ASTM-A-240 | |||||||||
| AMS Standard | AMS-5510 | |||||||||
| Alloy Steel Type | Stainless Steel | |||||||||
| Temper | Annealed Temper | |||||||||
| Minimum Elongation in 2 Inch (in) (0.002 to 0.003 Inch (in) Thick) | 20 % | |||||||||
| Minimum Elongation in 2 Inch (in) (0.003 to 0.004 Inch (in) Thick) | 30 % | |||||||||
| Minimum Elongation in 2 Inch (in) (Over 0.004 Inch (in) Thick) | 40 % | |||||||||
| Maximum Carbon Composition | 0.08 % | |||||||||
| Maximum Manganese Composition | 2.00 % | |||||||||
| Maximum Silicon Composition | 1.00 % | |||||||||
| Maximum Phosphorus Composition | 0.04 % | |||||||||
| Maximum Sulfur Composition | 0.03 % | |||||||||
| Maximum Chromium Composition | 19 % | |||||||||
| Maximum Nickel Composition | 12 % | |||||||||
| Maximum Molybdenum Composition | 0.75 % | |||||||||
| Maximum Copper Composition | 0.75 % | |||||||||
| Minimum Yield Strength (0.2 Percent (%) Offset) | 25 ksi | |||||||||
| Maximum Titanium Composition | 0.70 % | |||||||||
| Maximum Nitrogen Composition | 0.10 % | |||||||||
| Minimum Tensile Strength (0.002 to 0.003 Inch (in) Thick) | 70 to 110 ksi | |||||||||
| Minimum Tensile Strength (0.003 to 0.004 Inch (in) Thick) | 70 to 105 ksi | |||||||||
| Minimum Tensile Strength (Over 0.004 Inch (in) Thick) | 70 to 100 ksi | |||||||||
|
|
||||||||||